聚醚醚酮,膜, PEEK, 0.25mm厚
产品介绍
订货号 | 包装规格 | Sizes | 846-421-38 | 100 mm x 100 mm | 802-672-49 | 150 mm x 150 mm | 334-051-28 | 300 mm x 300 mm | Coil | 756-401-47 | 0.5 m | 550-181-00 | 1 m | 772-635-66 | 2 m | 207-879-14 | 5 m | 881-161-49 | 10 m |
产品参数 Coil Width[卷材宽度] | 610mm | Grade[等级] | VICTREX® APTIV® 2000 | Structure[结构] | Amorphous | Surface Finish[表面光洁度] | Matt/Gloss | Thickness[厚度] | 0.25mm | Transparency[透明度] | Transparent Pale Amber | Chemical Resistance(耐化学性) | Acids - concentrated | Good-Poor | Acids - dilute | Good | Alcohols | Good | Alkalis | Good | Aromatic hydrocarbons | Good | Greases and Oils | Good | Halogenated Hydrocarbons | Good | Halogens | Good-Poor | Ketones | Good-Poor | Thermal Properties(热性能) | Coefficient of thermal expansion ( x10⁻⁶ K⁻¹ ) | 47.000 - 108.000 | Heat-deflection temperature - 0.45MPa ( C ) | > 260 | Heat-deflection temperature - 1.8MPa ( C ) | 160.0 | Specific heat ( J K⁻¹ kg⁻¹ ) | 1340.0 | Thermal conductivity ( W m⁻¹ K⁻¹ ) | 0.25 @23℃ | Upper working temperature ( C ) | 250 | Physical Properties(物理性质) | Density ( g cm⁻³ ) | 1.260 - 1.320 | Flammability | V-0@1.5mm | Limiting oxygen index ( % ) | 35 | Radiation resistance | Good | Resistance to Ultra-violet | Fair | Water absorption - equilibrium ( % ) | 0.50 | Water absorption - over 24 hours ( % ) | 0.100 - 0.300 | Mechanical Properties(机械性能) | Coefficient of friction | 0.18 | Elongation at break ( % ) | 50.0 | Hardness - Rockwell | M99 | Izod impact strength ( J m⁻¹ ) | 85.0 | Poisson's ratio | 0.400 | Tensile modulus ( GPa ) | 3.70 - 4.00 | Tensile strength ( MPa ) | 70.00 - 100.00 | Electrical Properties(电气特性) | Dielectric constant @1kHz | 3.20 - 3.30 @50Hz-10Khz | Dielectric strength ( kV mm⁻¹ ) | 190.0 @50μm | Dissipation factor @ 1MHz | 0.0030 | Volume resistivity ( Ohmcm ) | 10¹⁵-10¹⁶ |
其他参数 公差 直径 | <100mm | ±1mm |
---|
≥100mm | +2% / -1% | 厚度 | | ±20% |
---|
长度 1 | <100mm | ±1mm |
---|
≥100mm | +2% / -1% | 长度 2 | <100mm | ±1mm |
---|
≥100mm | +2% / -1% |
| |
Goodfellow(顾特服)电话: 点击&查看18024074014地址:
同品牌产品:
相关产品:
|